Product Description
Chrome Plating and Steel Oxidation Line, new, still packed in containers Coating thickness 20 mcr, max part size 500x50x50 mm
MACHINE REF :13818
Machines For Sale — . Miscellaneous
MAKE :Chrome Plating and Steel Oxidation Line, new, still packed in containers
MODEL :Coating thickness 20 mcr, max part size 500x50x50 mm
FURTHER SPECIFICATION :The size of parts for coating with hard chromium with a thickness of 10-20 microns at the request of the Customer must be 500x50x50 mm, the size of the parts in the photo is dia. 25mm, length 370mm.
Performance – 100 pcs/ day. With an 8-hour work shift, the bath is 7 hours.
The exposure time of the parts in the bath 30 – 40 min, loading bath – 10 parts. Therefore, to perform the program, one bath is enough. The line is mechanized, the auto operator is controlled from the button.
Line is consist of:
No. 1 – bath of drying parts, 1500x600x1000 mm, hot air blowing, T-ra 60-70С, time – 10-15 minutes, material – stainless. steel;
No. 2 – hot finish bath, 1500x600x1000mm, desalted water, running water, 0.1 rpm, T-ra 50-60С, time – 2 – 3 min, material – stainless steel;
No. 3 – a table for measuring and dismantling parts, 600x600x1000mm, material – stainless. steel;
No. 4 – cascade washing bath, 1500x1200x1000mm, tap water, running water, 0.3 rpm, T-ra 18-25С, time – 2 – 3 min, material – polypropylene;
No. 5 – bathtub collection of electrolyte, 1500x600x1000mm, tap water, temperature T-ra 18-25 С, time – 1 – 2 min, material – polypropylene;
No. 6 – bath of hard chrome plating, 600x1500x1000mm, composition: chromic anhydride – 120-150 g / l, sulfuric acid – 1.2-1.5 g / l; mode: dense current – 60 – 80a / sq. dm, T-ra – 50-60 C, time – 30 – 40 min; material – vinyl plastic;
No. 7 – table for mounting parts, 600x600x1000mm, material – stainless. steel;
No. 8 – cascade washing bath, 1500x1200x1000mm, tap water, running water, 0.3 rpm, T-ra 18-25С, time – 2 – 3 min, material – polypropylene;
No. 9 – activation bath, 1500x1200x1000mm, hydrochloric acid – 100-200 g / l, T-ra 18-25С, time – 0.5 – 1.0 min, material – polypropylene;
No. 10 – pickling bath, composition: hydrochloric acid – 300 g / l, inhibitor – Friend plus 2x – 5 ml / l; mode: T-ra 18-25 C, time – 4 min; material – polypropylene;
No. 11 – cold washing bath, 1500x600x1000mm, tap water, flow water, 0.3 rpm, T-ra – 18 – 25 С; time – 2 – 3 min, material polypropylene;
No. 12 – hot flush bath, 1500x600x1000 mm, tap water, flow water, 0.3 rpm, T-ra – 40-50 ° C; time – 1 – 2 min, material – polypropylene;
No. 13 – degreasing bath, 1500x600x1000 mm, composition: TMS E-Klin 148E – 50 – 120 ml / l; mode: T-ra – 40 – 65 С; time – 5 – 10 min; material – stainless steel;
No. 14 – steel oxidation bath, 1500x600x1000mm, composition: caustic soda 600 – 700 g / l, sodium nitrate – 200-250 g / l; mode: T-ra 150 – 155 С, time – 40-60 min; material – steel St3;
No. 15 – hot flushing bath, 1500x600x1000 mm, tap water, flow water, 0.3 rpm, T-ra – 40-50 ° C; time – 3-4 minutes, material – polypropylene;
No. 16 – oil impregnation bath 1500x600x1000mm, mineral oil – spun, T-ra 105-120 С, time – 5 – 10 min; material – steel St3;
No. 17 – a place for draining oil and wiping parts, 1500x600x1000mm, material – steel St3;
Description
Chrome Plating and Steel Oxidation Line, new, still packed in containers Coating thickness 20 mcr, max part size 500x50x50 mm